"POLYLAC®" PA-765 data provided by IDES
Page 1 of 3
POLYLAC® PA-765
Units: English
CHI MEI CORPORATION - Acrylonitrile Butadiene Styrene Product Characteristics
Material Status Availability
l l l l l l
Test Standards Available
l l l
Additive Recycled Content Features
l l l l
Forms Processing Method
l l
Commercial: Active l South America Middle East Latin America l Pacific Rim l Europe Africa l North America Australia Asia ASTM DIN ISO Ignition Resistant No Extinguishing, Self l Flame Retardant l Impact Resistance, Medium Flow, High Pellets Injection Molding Properties
Physical
Density -Specific Gravity Melt Flow Rate (200 °C/5.0 kg - G) Mold Shrink, Linear-Flow (0.125 in) Mechanical
Tensile Modulus (73 °F) Tensile Strength Tensile Strength @ Yield (73 °F) Tensile Elongation @ Brk (73 °F) Flexural Modulus (73 °F) Flexural Strength Flexural Strength @ Yield (73 °F) Impact
Notched Izod Impact (73 °F, 0.125 in) (73 °F, 0.250 in) Hardness
Rockwell Hardness (R-Scale) Thermal
DTUL @264psi - Annealed DTUL @264psi - Unannealed DTUL @66psi - Unannealed Vicat Softening Point CLTE, Flow Electrical
Volume Resistivity Arc Resistance Ignition Characteristics
UL File Number Flame Rating - UL (0.0591 in) (0.0984 in) (0.0984 in)
1
Nominal Values (English)
1.19 sp gr 23/23°C 5.20 g/10 min 0.0030 to 0.0070 in/in Nominal Values (English)
360000 5530 5500 15 300000 8800 8800
psi psi psi % psi psi psi
Nominal Values (English)
Test Method
ASTM D792 ASTM D1238 ASTM D955 Test Method
ASTM D638 ASTM D638 ASTM D638 ASTM D638 ASTM D790 ASTM D790 ASTM D790 Test Method
ASTM D256 4.00 ft-lb/in 3.30 ft-lb/in Nominal Values (English)
100
ASTM D785
Nominal Values (English)
181 163 181 194 7.2E -005
Test Method
°F °F °F °F in/in/°F
Nominal Values (English)
1.0E+015 ohm-cm 7.00 sec Nominal Values (English)
Test Method
ASTM D648 ASTM D648 ASTM D648 ASTM D1525 ASTM D696 Test Method
ASTM D257 ASTM D495 Test Method
E56070 UL 94 V-0 5VA V-0
"POLYLAC®" PA-765 data provided by IDES
Page 2 of 3
(0.118 in) (0.118 in) (0.0591 in)
V-0 5VA 5VB
UL 746
Nominal Values (English)
Rel Temp Indx Mech w/oImp (0.0591 in) (0.0984 in) (0.118 in) Rel Temp Indx Mech w/Imp (0.0591 in) (0.0984 in) (0.118 in) Rel Temp Indx Elect (0.0591 in) (0.0984 in) (0.118 in) Comparative Tracking Index (CTI) (PLC) High Voltage Arc Tracking Rate (HVTR) (PLC) Hot-wire Ignition (HWI) (PLC) (0.118 in) (0.0984 in) (0.0591 in) High Amp Arc Ignition (HAI) (PLC) (0.118 in) (0.0984 in) (0.0591 in)
Test Method
UL 746 176 °F 176 °F 176 °F UL 746 176 °F 176 °F 176 °F UL 746 176 °F 176 °F 176 °F PLC 1 PLC 0
UL 746 UL 746 UL 746
PLC 0 PLC 2 PLC 0 UL 746 PLC 0 PLC 0 PLC 0
Additional Properties
Melt Flow Rate, ASTM D-1238, Condition G: 5.2 g/10 min Volume Resistivity, ASTM D257: > 1E 15 ohm-cm Impact Flexural Test, ISO 179/2C, Notched: 12 kJ/m ² Impact Flexural Test, ISO 179/2D, Unnotched: No Break Vicat Softening Temp, DIN 53460, 50°C/hr ; 1 kg: 89°C Vicat Softening Temp, DIN 53460, 50°C/hr ; 5 kg: 78°C Vicat Softening Temp, DIN 53460, 120 °C/hr ; 1 kg: 90°C Vicat Softening Temp, DIN 53460, 120 °C/hr ; 5 kg: 80°C DTUL @ 1.80 MPa, DIN 53461, Unannealed: 68°C DTUL @ 1.80 MPa, DIN 53461, Annealed: 90 °C Impact Flexural Test, DIN 53453, Notched: 12 kJ/m² Impact Flexural Test, DIN 53453, Unnotched: No Break Tensile Strength @ Yield, DIN 53455, 50 mm/min: 39 MPa Tensile Strength @ Break, DIN 53455, 50 mm/min: 34 MPa Tensile Elongation, DIN 53455, 50 mm/min: 10% Flexural Strength, DIN 53452, 2 mm/min: 55 MPa Flexural Modulus, DIN 53452, 2 mm/min: 1.8 GPa Mass Density, DIN 53479 -A, 23°C: 1.8 g/cm³ Processing Information Injection Molding Parameters
Drying Temperature Drying Time Suggested Max Moisture Suggested Max Regrind Suggested Shot Size Rear Temperature Middle Temperature Front Temperature Nozzle Temperature Processing (Melt) Temp
Nominal Values (English)
175 to 185 3.0 0.10 20 40 to 80 330 to 350 345 to 365 355 to 375 345 to 365 395
°F hr % % % °F °F °F °F °F
Test Method
"POLYLAC®" PA-765 data provided by IDES
Page 3 of 3
Mold Temperature Injection Pressure Injection Rate Holding Pressure Back Pressure Screw Speed
105 to 160 710 to 850 Slow-Moderate 570 to 710 70.0 to 140 50 to 90 Notes
1
Typical properties; not to be construed as specifications.
°F psi psi psi rpm